OERLIKON OVERCORD F AWS SFA 5.1 : E 6013 WELDING ELECTRODE

OERLIKON OVERCORD F
For welding unalloyed and low alloy steels, rutile cellulosic covering

Application & Properties:
General-purpose electrode for structural, steelwork, workshop and maintenance welding, specially suited for vertical-down welding and tack-welds. Good gap bridging. Can be used on galvanized, primer painted and slightly rusted parts. In assembly welding, electrode can be used with the same current setting in all positions. Smooth, slightly concave welds blending into base metal without undercutting. Slag in most cases self-releasing.

Aplikasi & Penggunaan:
Kawat las untuk aplikasi umum, sangat cocok untuk pengelasan pada konstruksi, bengkel las, repair & maintenace, khususnya untuk pengelasan dengan posisi vertical-down dan semua posisi lainnya. Baik untuk pengelasan pada celah. Dapat digunakan pada besi galvanis, besi yang sudah dicat dasar, besi yang agak berkarat. Kawat las ini memiliki keistimewaan: alur lasnya halus, penetrasinya dalam, tanpa terjadi undercut, dan terak pada umumnya dapat terlepas sendiri.

International Standards:
AWS SFA 5.1 : E 6013
DIN 1913 : E 43 22 R (C) 3
DIN EN 499 : E 38 0 RC 11
 

Approvals : BKI, LRS, GL

Mechanical Properties:
Yield strength : > 380 N/mm2
Tensile strength : 470 - 600 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 80 J

Chemical Analysis (%):
C: 0,08 Mn: 0,5 Si: 0,3

Redrying: Generally not required.
If necesarry; redry at 100-110oC / 1 h

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON ZELCORD Fe / ZELCORD 60 AWS SFA 5.1 : E 6010 WELDING ELECTRODE

OERLIKON  ZELCORD Fe / Zelcord 60 
For welding unalloyed and low alloy steels, cellulosic covering

Application & Properties:
Electrode for welding girth seams of pipe lines, applying the vertical-down technique.  It is suitable  for welding root passes, filler and cover passes. OERLIKON ZELCORD Fe / ZELCORD 60 is also suited for depositing root passes on high-strength pipe steels.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan pipa dengan teknik vertical-down. Sangat cocok untuk pengelasan root pass, filler dan cover pass. Kawat las OERLIKON ZELCORD Fe / ZELCORD 60 juga cocok untuk pengelasan root pass pada pipa baja yang tensile strength-nya tinggi.

International Standards:
AWS SFA 5.1 :  E 6010
DIN 1913 :  E 43 43 C 4
DIN EN 499 :  E 35 2 C 25

Mechanical Properties:
Yield strength :  410 N/mm2
Tensile strength :  480 N/mm2
Elongation :  28 %
Impact Charpy
+20oC :  100 J
 -20oC :  70 J

Chemical Analysis (%):
C: 0,1      Mn: 0,6      Si: 0,2

Redrying: Do not redry!

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON ZELCORD Mo / ZELCORD 70 AWS SFA 5.1 : E 7010-P1 WELDING ELECTRODE

OERLIKON  ZELCORD Mo / Zelcord 70 
For welding unalloyed and low alloy steels, cellulosic covering

Application & Properties:
Electrode for welding girth seams of pipe lines, applying the vertical-down technique. It is suited for welding root passes, hot passes, filler and cover passes.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan pipa dengan  teknik vertical-down.  Sangat cocok untuk  pengelasan root pass, filler dan cover pass.

International Standards:
AWS SFA 5.1 :  E 7010-P1
DIN EN 499 :  E 38 2 Mo C 25

Mechanical Properties:
Yield strength :  460 N/mm2
Tensile strength :  550 N/mm2
Elongation :  24 %
Impact Charpy
+20oC :  90 J
 -20oC :  65 J

Chemical Analysis (%):
C: 0,1    Mn: 0,4    Si: 0,2    Mo: 0,4

Redrying: Do not redry!

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON FERROMATIC AWS SFA 5.1 : E 7024 WELDING ELECTRODE

 OERLIKON FERROMATIC
For welding unalloyed and low alloy steels, thick rutile covering

Application & Properties:
High-efficiency electrode having a weld metal recovery of approx. 165%. High melt-off rates, short welding times and long welds to be achieved, guarantee the economical execution of fillet welds. In welding, the tip of the electrode is dragged on the work, thus producing optimum-shaped concave fillets. It is suited for welding primer painted plates. Very good arc striking and restriking. Clean and smooth welds blending into base metal without undercuts. With proper current setting, slag is self releasing.

Aplikasi & Penggunaan:
Kawat las ini memiliki efisiensi tinggi hingga 165%. Kecepatan pencairan kawat inti sangat tinggi, waktu pengelasannya pendek, alur las yang dihasilkan sangat panjang. Sangat cocok untuk pengelasan pada posisi fillet.   Pengelasan dapat dilakukan dengan cara menempelkan kawat las pada material, sehingga alur lasnya memiliki bentuk cekung secara optimal pada posisi fillet. Dapat digunakan pada baja yang sudah dicat dasar. Kestabilan nyala api dan restrikingnya sangat baik. Alur lasnya halus dan bersih, penetrasinya dalam tanpa undercut. Dengan menggunakan ampere yang sesuai, terak dapat terlepas sendiri.

International Standards:
AWS SFA 5.1 : E 7024
DIN EN 499 : E 42 0 RR 73
DIN 1913 : E 51 32 RR 11 160

Mechanical Properties:
Yield strength : > 420 N/mm2
Tensile strength : 510 - 610 N/mm2
Elongation : > 22 %
Impact Charpy
+20oC : 80 J

Chemical Analysis (%):
C: 0,1 Mn: 0,9 Si: 0,45

Redrying: Generally not required.
If necesarry; redry at 100-110oC / 1 h

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON SPEZIAL AWS SFA 5.1 : E 7016 WELDING ELECTRODE

 OERLIKON SPEZIAL
For welding unalloyed and low alloy steels, basic covering

Application & Properties:
Multi-purpose electrode suitable for structural steelwork, workshop, and maintenance welding. Smooth and clean welds, blending into base metal without undercuts. Excellent gap bridging properties. The covering of this electrode produces a stable, concentrated and directed arc, thus being ideally suited for root pass and positional welding. Welds are X-ray quality.

Aplikasi & Penggunaan:
Kawat las multi fungsi untuk industri konstruksi, repair & maintenance. Alur lasnya halus dan bersih, penetrasinya dalam tanpa terjadi undercut. Baik untuk pengelasan pada celah. Kawat las memiliki kestabilan nyala api yang sangat baik, terfokus, dan stabil, sehingga cocok untuk pengelasan root pass dan pengelasan pada segala posisi. Alur las memiliki performa X-Ray yang sangat baik.

International Standards:

AWS SFA 5.1 : E 7016
DIN 1913 : E 51 43 B (R) 10
DIN EN 499 : E 38 2 B 12 H 10

Mechanical Properties:
Yield strength : > 380 N/mm2
Tensile strength : 470 - 600 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 150 J
-20oC : 80 J

Chemical Analysis (%):
C: 0,06 Mn: 0,9 Si: 0,7

Redrying:
Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON SUPERCITO AWS SFA 5.1 : E 7018 WELDING ELECTRODE

OERLIKON SUPERCITO
For welding unalloyed and low alloy steels, basic covering

Application & Properties:
Basic electrode for producing tough and crack-free welded joints even on steels having a carbon content of up to 0,4%. Weld metal recovery amounts to approx. 120%. Good operating characteristics, also in positional welding. Weld metal exhibits good toughness properties down to -60oC. Electrode is suitable for depositing buffer layers on higher carbon steels.

Aplikasi & Penggunaan:
Kawat las dengan coating type basic yang memiliki alur las yang ulet, dan bebas terjadi keretakan bahkan pada baja yang memiliki kadar karbon hingga 0,4%. Efisiensi pengelasannya 120%. Karakter pengelasannya sangat baik pada segala posisi. Alur las memiliki keuletan yang sangat baik pada temperatur hingga -60oC. Kawat las dapat digunakan sebagai buffer layer pada baja karbon tinggi.

International Standards:
AWS SFA 5.1 : E 7018
DIN 1913 : E 51 55 B 10
DIN EN 499 : E 42 5 B 42 H 10

Mechanical Properties:
Yield strength : > 420 N/mm2
Tensile strength : 500 - 640 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 200 J
-60oC : 70 J

Chemical Analysis (%):
C: 0,08 Mn: 1,1 Si: 0,5

Redrying:
Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON TENACITO WZ AWS SFA 5.1 : E 7016-1 WELDING ELECTRODE

OERLIKON  TENACITO WZ 
For welding normalized and normalized + tempered fine grain and special structural steels,
basic covering

Application & Properties:
Electrode producing tough and crack-free welded joints. Suited for welding steels having a carbon content of up to 0,6%. The weld metal has a very low hydrogen content and is resistant to ageing. Electrode approved for rail joint welding and CTOD-tested for offshore applications. Particularly suited for welding root passes and for bridging wide gaps. The electrode features a stable and concentrated arc, making it well-suited for positional welding. Welds are of X-ray quality. Good operating characteristics, even on AC.
 
Aplikasi & Penggunaan:
Kawat las ini sangat cocok untuk pengelasan pada baja yang memiliki kadar karbon hingga 0,6%. Hasil lasnya memiliki kadar hidrogen yang sangat rendah serta memiliki kekuatan yang sangat baik. Sangat direkomendasikan untuk pengelasan pada proyek offshore. Keunggulan lainnya adalah: alur las yang sangat ulet dan sambungan yang bebas retak. Sangat cocok untuk pengelasan root pass dan pengelasan pada celah yang lebar.  Kawat las memiliki kestabilan nyala api yang baik dan terfokus, sehingga dapat digunakan pada segala posisi. Alur las memiliki performa X-ray yang baik. Karakter pengelasannya sangat baik, bahkan pada arus AC.

International Standards:
AWS SFA 5.1 :  E 7016-1
DIN 8529 :  E SY 42 76 Mn B
DIN EN 499 :  E 46 5 B 32 H 5

Mechanical Properties:
Yield strength :  > 420 N/mm2
Tensile strength :  500 - 640 N/mm2
Elongation :  > 20 %
Impact Charpy
+20oC :  200 J
 -60oC :  100 J

Chemical Analysis (%):
C: 0,06 Mn: 1,5 Si: 0,3

Redrying: Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com