For welding normalized and normalized + tempered fine grain and special structural steels,
basic covering
Application & Properties:
Electrode producing tough and crack-free welded joints. Suited for welding steels having a carbon content of up to 0,6%. The weld metal has a very low hydrogen content and is resistant to ageing. Electrode approved for rail joint welding and CTOD-tested for offshore applications. Particularly suited for welding root passes and for bridging wide gaps. The electrode features a stable and concentrated arc, making it well-suited for positional welding. Welds are of X-ray quality. Good operating characteristics, even on AC.
Aplikasi & Penggunaan:
Kawat las ini sangat cocok untuk pengelasan pada baja yang memiliki kadar karbon hingga 0,6%. Hasil lasnya memiliki kadar hidrogen yang sangat rendah serta memiliki kekuatan yang sangat baik. Sangat direkomendasikan untuk pengelasan pada proyek offshore. Keunggulan lainnya adalah: alur las yang sangat ulet dan sambungan yang bebas retak. Sangat cocok untuk pengelasan root pass dan pengelasan pada celah yang lebar. Kawat las memiliki kestabilan nyala api yang baik dan terfokus, sehingga dapat digunakan pada segala posisi. Alur las memiliki performa X-ray yang baik. Karakter pengelasannya sangat baik, bahkan pada arus AC.
International Standards:
AWS SFA 5.1 : E 7016-1
DIN 8529 : E SY 42 76 Mn B
DIN EN 499 : E 46 5 B 32 H 5
Mechanical Properties:
Yield strength : > 420 N/mm2
Tensile strength : 500 - 640 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 200 J
-60oC : 100 J
Chemical Analysis (%):
C: 0,06 Mn: 1,5 Si: 0,3
Redrying: Required at 200oC for 2 hrs