For welding stainless and heat resisting steels, basic covering
Application & Properties:
Electrode for joining dissimilar steels and depositing claddings on ferritic steels. The weld metal consists of austenitic Cr-Ni-Mo steel with possible small amounts of delta-ferrite. It is non-scaling up to +850oC. The weld metal is highly crack-resistant and therefore suited to joining difficult-to-weld steels and depositing stress-relaxing buffer layers on crack sensitive base metal or underneath hard facing deposits. Highest operating temperature for dissimilar steel joints is +300oC. In case of higher temperatures, use OERLIKON SUPRANEL 600 electrodes. Weld metal work-hardens.
Aplikasi & Penggunaan:
Kawat las untuk penyambungan baja yang tidak sama jenisnya. Hasil las memiliki struktur austenite chromium-nikel-molybdenum dan sedikit mengandung struktur delta ferrite. Ketahanannya terhadap scaling bisa mencapai hingga temperatur 850oC. Kawat las memiliki ketahanan terhadap keretakan yang sangat baik dan sangat cocok untuk penyambungan baja yang sulit dilas serta sebagai buffer layer yang ulet untuk pengelasan baja yang sangat sensitif terhadap keretakan, atau sebagai landasan sebelum dilakukan pengelasan hard facing. Temperatur operasi untuk penyambungan baja yang tidak sama jenisnya bisa mencapai hingga temperatur 300oC. Hasil las dapat di-work-hardening.
International Standards:
AWS SFA 5.4 : E 307-15
DIN EN 1600 : E 18 8 Mn B 22
DIN 8556 : E 18 8 Mn B 20 +
Mechanical Properties:
Yield strength : 400 N/mm2
Tensile strength : 650 N/mm2
Elongation : 35 %
Impact Charpy
+20oC : 100 J
-60oC : 60 J
Chemical Analysis (%):
C: 0,12 Mn: 6 Si: 0,4
Cr: 19 Ni: 9
Redrying: 200oC for 2 hrs