For heterogeneous welding of cast iron, basic covering
Application & Properties:
Electrode having a nickel-iron core wire for welding cast iron without or with low preheating of up to +300oC. The weld metal features a low coefficient of thermal expansion and as a result, little shrinkage. It has higher strength properties than pure nickel weld metal and is therefore preferable used for welding nodular cast iron, white and black heart malleable cast iron, as well as austenitic nodular cast iron or joining these metals to components made of steel, copper or nickel materials. Easy arc striking and restriking, stable arc, smooth bead. Weld metal is machinable. Weld short beads.
Aplikasi & Penggunaan:
Kawat las dengan kawat inti ferro-nikel untuk pengelasan ancuran dengan atau tanpa pemanasan awal hingga 300oC. Alur las memiliki keunggulan: koefisien muai panasnya yang rendah, sehingga shrinkagenya sangat kecil. Kekuatannya lebih tinggi dari kawat las nickel murni sehingga sangat cocok untuk pengelasan baja ancuran type nodular, putih, dan hitam malleable, serta ancuran nodular austenite atau penyambungan material ferro-nikel dengan besi, tembaga atau dengan material nikel. Striking dan restrikingnya sangat mudah, kestabilan nyala apinya sangat mudah, alur lasnya sangat baik. Hasil las dapat dibubut.
International Standards:
AWS SFA 5.15 : E NiFeC1
DIN 8573 : E NiFe-1 BG 22
Mechanical Properties:
Hardness : 170 HB
Yield strength : 300 N/mm2
Tensile strength : 450 N/mm2
Elongation : 10%
Chemical Analysis (%):
C: 0,5 Ni: 53 Fe: Rest
Redrying: 100 - 110oC for 1 hr