OERLIKON OVERCORD F AWS SFA 5.1 : E 6013 WELDING ELECTRODE

OERLIKON OVERCORD F
For welding unalloyed and low alloy steels, rutile cellulosic covering

Application & Properties:
General-purpose electrode for structural, steelwork, workshop and maintenance welding, specially suited for vertical-down welding and tack-welds. Good gap bridging. Can be used on galvanized, primer painted and slightly rusted parts. In assembly welding, electrode can be used with the same current setting in all positions. Smooth, slightly concave welds blending into base metal without undercutting. Slag in most cases self-releasing.

Aplikasi & Penggunaan:
Kawat las untuk aplikasi umum, sangat cocok untuk pengelasan pada konstruksi, bengkel las, repair & maintenace, khususnya untuk pengelasan dengan posisi vertical-down dan semua posisi lainnya. Baik untuk pengelasan pada celah. Dapat digunakan pada besi galvanis, besi yang sudah dicat dasar, besi yang agak berkarat. Kawat las ini memiliki keistimewaan: alur lasnya halus, penetrasinya dalam, tanpa terjadi undercut, dan terak pada umumnya dapat terlepas sendiri.

International Standards:
AWS SFA 5.1 : E 6013
DIN 1913 : E 43 22 R (C) 3
DIN EN 499 : E 38 0 RC 11
 

Approvals : BKI, LRS, GL

Mechanical Properties:
Yield strength : > 380 N/mm2
Tensile strength : 470 - 600 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 80 J

Chemical Analysis (%):
C: 0,08 Mn: 0,5 Si: 0,3

Redrying: Generally not required.
If necesarry; redry at 100-110oC / 1 h

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON ZELCORD Fe / ZELCORD 60 AWS SFA 5.1 : E 6010 WELDING ELECTRODE

OERLIKON  ZELCORD Fe / Zelcord 60 
For welding unalloyed and low alloy steels, cellulosic covering

Application & Properties:
Electrode for welding girth seams of pipe lines, applying the vertical-down technique.  It is suitable  for welding root passes, filler and cover passes. OERLIKON ZELCORD Fe / ZELCORD 60 is also suited for depositing root passes on high-strength pipe steels.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan pipa dengan teknik vertical-down. Sangat cocok untuk pengelasan root pass, filler dan cover pass. Kawat las OERLIKON ZELCORD Fe / ZELCORD 60 juga cocok untuk pengelasan root pass pada pipa baja yang tensile strength-nya tinggi.

International Standards:
AWS SFA 5.1 :  E 6010
DIN 1913 :  E 43 43 C 4
DIN EN 499 :  E 35 2 C 25

Mechanical Properties:
Yield strength :  410 N/mm2
Tensile strength :  480 N/mm2
Elongation :  28 %
Impact Charpy
+20oC :  100 J
 -20oC :  70 J

Chemical Analysis (%):
C: 0,1      Mn: 0,6      Si: 0,2

Redrying: Do not redry!

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON ZELCORD Mo / ZELCORD 70 AWS SFA 5.1 : E 7010-P1 WELDING ELECTRODE

OERLIKON  ZELCORD Mo / Zelcord 70 
For welding unalloyed and low alloy steels, cellulosic covering

Application & Properties:
Electrode for welding girth seams of pipe lines, applying the vertical-down technique. It is suited for welding root passes, hot passes, filler and cover passes.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan pipa dengan  teknik vertical-down.  Sangat cocok untuk  pengelasan root pass, filler dan cover pass.

International Standards:
AWS SFA 5.1 :  E 7010-P1
DIN EN 499 :  E 38 2 Mo C 25

Mechanical Properties:
Yield strength :  460 N/mm2
Tensile strength :  550 N/mm2
Elongation :  24 %
Impact Charpy
+20oC :  90 J
 -20oC :  65 J

Chemical Analysis (%):
C: 0,1    Mn: 0,4    Si: 0,2    Mo: 0,4

Redrying: Do not redry!

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON FERROMATIC AWS SFA 5.1 : E 7024 WELDING ELECTRODE

 OERLIKON FERROMATIC
For welding unalloyed and low alloy steels, thick rutile covering

Application & Properties:
High-efficiency electrode having a weld metal recovery of approx. 165%. High melt-off rates, short welding times and long welds to be achieved, guarantee the economical execution of fillet welds. In welding, the tip of the electrode is dragged on the work, thus producing optimum-shaped concave fillets. It is suited for welding primer painted plates. Very good arc striking and restriking. Clean and smooth welds blending into base metal without undercuts. With proper current setting, slag is self releasing.

Aplikasi & Penggunaan:
Kawat las ini memiliki efisiensi tinggi hingga 165%. Kecepatan pencairan kawat inti sangat tinggi, waktu pengelasannya pendek, alur las yang dihasilkan sangat panjang. Sangat cocok untuk pengelasan pada posisi fillet.   Pengelasan dapat dilakukan dengan cara menempelkan kawat las pada material, sehingga alur lasnya memiliki bentuk cekung secara optimal pada posisi fillet. Dapat digunakan pada baja yang sudah dicat dasar. Kestabilan nyala api dan restrikingnya sangat baik. Alur lasnya halus dan bersih, penetrasinya dalam tanpa undercut. Dengan menggunakan ampere yang sesuai, terak dapat terlepas sendiri.

International Standards:
AWS SFA 5.1 : E 7024
DIN EN 499 : E 42 0 RR 73
DIN 1913 : E 51 32 RR 11 160

Mechanical Properties:
Yield strength : > 420 N/mm2
Tensile strength : 510 - 610 N/mm2
Elongation : > 22 %
Impact Charpy
+20oC : 80 J

Chemical Analysis (%):
C: 0,1 Mn: 0,9 Si: 0,45

Redrying: Generally not required.
If necesarry; redry at 100-110oC / 1 h

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON SPEZIAL AWS SFA 5.1 : E 7016 WELDING ELECTRODE

 OERLIKON SPEZIAL
For welding unalloyed and low alloy steels, basic covering

Application & Properties:
Multi-purpose electrode suitable for structural steelwork, workshop, and maintenance welding. Smooth and clean welds, blending into base metal without undercuts. Excellent gap bridging properties. The covering of this electrode produces a stable, concentrated and directed arc, thus being ideally suited for root pass and positional welding. Welds are X-ray quality.

Aplikasi & Penggunaan:
Kawat las multi fungsi untuk industri konstruksi, repair & maintenance. Alur lasnya halus dan bersih, penetrasinya dalam tanpa terjadi undercut. Baik untuk pengelasan pada celah. Kawat las memiliki kestabilan nyala api yang sangat baik, terfokus, dan stabil, sehingga cocok untuk pengelasan root pass dan pengelasan pada segala posisi. Alur las memiliki performa X-Ray yang sangat baik.

International Standards:

AWS SFA 5.1 : E 7016
DIN 1913 : E 51 43 B (R) 10
DIN EN 499 : E 38 2 B 12 H 10

Mechanical Properties:
Yield strength : > 380 N/mm2
Tensile strength : 470 - 600 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 150 J
-20oC : 80 J

Chemical Analysis (%):
C: 0,06 Mn: 0,9 Si: 0,7

Redrying:
Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON SUPERCITO AWS SFA 5.1 : E 7018 WELDING ELECTRODE

OERLIKON SUPERCITO
For welding unalloyed and low alloy steels, basic covering

Application & Properties:
Basic electrode for producing tough and crack-free welded joints even on steels having a carbon content of up to 0,4%. Weld metal recovery amounts to approx. 120%. Good operating characteristics, also in positional welding. Weld metal exhibits good toughness properties down to -60oC. Electrode is suitable for depositing buffer layers on higher carbon steels.

Aplikasi & Penggunaan:
Kawat las dengan coating type basic yang memiliki alur las yang ulet, dan bebas terjadi keretakan bahkan pada baja yang memiliki kadar karbon hingga 0,4%. Efisiensi pengelasannya 120%. Karakter pengelasannya sangat baik pada segala posisi. Alur las memiliki keuletan yang sangat baik pada temperatur hingga -60oC. Kawat las dapat digunakan sebagai buffer layer pada baja karbon tinggi.

International Standards:
AWS SFA 5.1 : E 7018
DIN 1913 : E 51 55 B 10
DIN EN 499 : E 42 5 B 42 H 10

Mechanical Properties:
Yield strength : > 420 N/mm2
Tensile strength : 500 - 640 N/mm2
Elongation : > 20 %
Impact Charpy
+20oC : 200 J
-60oC : 70 J

Chemical Analysis (%):
C: 0,08 Mn: 1,1 Si: 0,5

Redrying:
Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON TENACITO WZ AWS SFA 5.1 : E 7016-1 WELDING ELECTRODE

OERLIKON  TENACITO WZ 
For welding normalized and normalized + tempered fine grain and special structural steels,
basic covering

Application & Properties:
Electrode producing tough and crack-free welded joints. Suited for welding steels having a carbon content of up to 0,6%. The weld metal has a very low hydrogen content and is resistant to ageing. Electrode approved for rail joint welding and CTOD-tested for offshore applications. Particularly suited for welding root passes and for bridging wide gaps. The electrode features a stable and concentrated arc, making it well-suited for positional welding. Welds are of X-ray quality. Good operating characteristics, even on AC.
 
Aplikasi & Penggunaan:
Kawat las ini sangat cocok untuk pengelasan pada baja yang memiliki kadar karbon hingga 0,6%. Hasil lasnya memiliki kadar hidrogen yang sangat rendah serta memiliki kekuatan yang sangat baik. Sangat direkomendasikan untuk pengelasan pada proyek offshore. Keunggulan lainnya adalah: alur las yang sangat ulet dan sambungan yang bebas retak. Sangat cocok untuk pengelasan root pass dan pengelasan pada celah yang lebar.  Kawat las memiliki kestabilan nyala api yang baik dan terfokus, sehingga dapat digunakan pada segala posisi. Alur las memiliki performa X-ray yang baik. Karakter pengelasannya sangat baik, bahkan pada arus AC.

International Standards:
AWS SFA 5.1 :  E 7016-1
DIN 8529 :  E SY 42 76 Mn B
DIN EN 499 :  E 46 5 B 32 H 5

Mechanical Properties:
Yield strength :  > 420 N/mm2
Tensile strength :  500 - 640 N/mm2
Elongation :  > 20 %
Impact Charpy
+20oC :  200 J
 -60oC :  100 J

Chemical Analysis (%):
C: 0,06 Mn: 1,5 Si: 0,3

Redrying: Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON INOX AW AWS SFA 5.4 : E 308L-16 WELDING ELECTRODE

OERLIKON INOX AW
For welding stainless and heat resisting steels, rutile covering

Application & Properties:
Electrode for welding austenitic stainless Cr-Ni steels or cast steels, having an extra low carbon content, as well as stainless or heat resisting chromium steels or cast steels. For operating temperatures of up to +350oC, non-scaling up to +800oC. Fine metal droplet transfer, good fusion of joint faces, finely rippled bead surface, easily removable slag. Easy arc striking and restriking.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan stainless steel chromium-nikel austenite, memiliki kadar karbon yang rendah. Temperatur operasinya bisa mencapai hingga di atas 350oC, ketahanannya terhadap scaling bisa mencapai temperatur hingga 800oC.   Penetrasinya dalam,  penyambungannya  sangat baik,  alur lasnya halus, terak mudah lepas. Kestabilan nyala api dan restrikingnya sangat baik.

International Standards:
AWS SFA 5.4 : E 308L-16
DIN EN 1600 : E 19 9 L R 12
DIN 8556 : E 19 9 L R 23

Mechanical Properties:
Yield strength : 400 N/mm2
Tensile strength : 580 N/mm2
Elongation : 35 %
Impact Charpy
+20oC : 65 J

Chemical Analysis (%):
C: 0,025 Mn: 0,8 Si: 0,9
Cr: 19 Ni: 10

Redrying:Required at 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON INOX BW AWS SFA 5.4 : E 316L-16 WELDING ELECTRODE

OERLIKON INOX BW
For welding stainless and heat resisting steels, rutile covering

Application & Properties:
Electrode for welding austenitic stainless Cr-Ni-Mo steels or cast steels, having an extra low carbon content. For operating temperatures of up to +400oC.   Fine metal droplet transfer,  good fusion of joint faces, finely rippled bead surface, easy slag removal, easy arc striking and restriking.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan stainless steel austenite chromium-nikel-molybdenum, memiliki kadar karbon yang rendah. Temperatur operasinya bisa mencapai hingga 400oC. Kawat las ini memiliki berbagai keunggulan antara lain: penetrasinya dalam, karakter penyambungannya sangat baik, alur lasnya bersih dan halus, terak mudah lepas, kestabilan nyala api dan restrikingnya sangat baik.

International Standards:
AWS SFA 5.4 : E 316L-16
DIN EN 1600 : E 19 12 3 L R 12
DIN 8556 : E 19 12 3 L R 36 23

Mechanical Properties:
Yield strength : 420 N/mm2
Tensile strength : 600 N/mm2
Elongation : 33 %
Impact Charpy (+20oC) : 60 J

Chemical Analysis (%):
C: 0,025 Mn: 0,8 Si: 0,9
Cr: 18,5 Ni: 12 Mo: 2,7

Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON INOX C AWS SFA 5.4 : E 310-15 WELDING ELECTRODE

OERLIKON INOX C
For welding stainless and heat resisting steels, basic covering

Application & Properties:
Electrode for welding heat resisting chromium and chromium-nickel steels as well as cast steels. Fully austenitic weld metal, non-scaling up to +1200oC. Weld metal is not corrosion resistant to sulphurous combustion gases.

Aplikasi & Penggunaan:
Kawat las untuk pengelasan stainless steel chromium dan chromium-nikel yang memerlukan ketahanan terhadap panas yang sangat tinggi, seperti halnya baja ancuran. Hasil lasnya memiliki struktur austenite, hasil las memiliki ketahanan terhadap scaling hingga temperatur 1200oC. Alur las tidak memiliki ketahanan korosi terhadap gas buang yang mengandung sulfur.

International Standards:
AWS SFA 5.4 : E 310-15
DIN EN 1600 : E 25 20 B 42
DIN 8556 : E 25 20 B 20 +

Mechanical Properties:

Yield strength : 400 N/mm2
Tensile strength : 600 N/mm2
Elongation : 35 %
Impact Charpy (+20oC) : 100 J

Chemical Analysis (%):
C: 0,1 Mn: 4,5 Si: 0,5
Cr: 25 Ni: 20

Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON INOX DW AWS SFA 5.4 : E 312-16 WELDING ELECTRODE

 OERLIKON INOX DW
For welding stainless and heat resisting steels, rutile covering

Application & Properties:
Electrode for joining dissimilar steels and depositing claddings on ferritic steels.  The ferritic-austenitic Cr-Ni weld metal contains approximately 50% of delta-ferrite and is non-scaling up to 1100oC. It features high resistance to cracking and is therefore suited to joining difficult-to-weld steels and depositing stress-relaxing buffer layers on crack sensitive base metals. Suitable for welding galvanized steel plates. Fine metal droplet transfer, good fusion of joint faces, finely rippled bead surface, easy slag removal, easy arc striking and restriking.
 
Aplikasi & Penggunaan:
Kawat las untuk penyambungan baja yang tidak sama jenisnya atau tidak diketahui jenisnya. Hasil lasnya memiliki struktur chromium-nikel ferrite-austenite yang mengandung 50% delta ferrite serta memiliki ketahanan terhadap scaling hingga temperatur 1100oC. Ketahanannya terhadap keretakan sangat baik, sangat cocok untuk pengelasan baja yang sulit dilas, buffer layer yang ulet pada baja yang sensitif terhadap keretakan. Penetrasinya dalam, karakter penyambungannya sangat baik, alur lasnya halus, pelepasan teraknya mudah, kestabilan nyala api dan restrikingnya sangat baik.

International Standards:
AWS SFA 5.4 : E 312-16
DIN EN 1600 : E 29 9 R 12
DIN 8556 : E 29 9 R 23

Mechanical Properties:
Yield strength : 450 N/mm2
Tensile strength : 750 N/mm2
Elongation : 20 %

Chemical Analysis (%):
C: 0,1 Mn: 1,0 Si: 1,1
Cr: 29 Ni: 10

Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON INOX AWL+Nb AWS SFA 5.4 : E 347-16 WELDING ELECTRODE

OERLIKON INOX AWL+Nb
For welding stainless and heat resisting steels, rutile covering

Application & Properties:
Electrode for welding stabilized austenitic stainless Cr-Ni steels  or  cast steels, as well as stainless or heat resisting Cr steels or cast steels. For operating temperatures of up to +400oC, non-scaling up to +800oC. Fine metal droplet transfer, good fusion of joint faces, finely rippled bead surface, easy slag removal, easy arc striking and restriking.
 
Aplikasi & Penggunaan:
Kawat las untuk pengelasan stainless steel chromium-nickel austenite seperti halnya baja ancuran dan stainless steel yang memerlukan ketahanan terhadap panas. Temperatur operasinya bisa mencapai 400oC, ketahanannya terhadap scaling bisa mencapai temperatur hingga 800oC. Kawat  las ini memiliki berbagai keistimewaan antara lain: penetrasinya dalam, karakter penyambungannya sangat baik, alur lasnya halus dan bersih, pelepasan teraknya sangat mudah, kestabilan nyala api dan restrikingnya sangat baik.

International Standards:
AWS SFA 5.4 : E 347-16
DIN EN 1600 : E 19 9 Nb R 12
DIN 8556 : E 19 9 Nb R 23

 
Mechanical Properties:
Yield strength : 420 N/mm2
Tensile strength : 620 N/mm2
Elongation : 33 %
Impact Charpy (+20oC) : 60 J

Chemical Analysis (%):
C: 0,025 Mn: 0,8 Si: 0,9
Cr: 19 Ni: 10 Nb: 0,4

Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON INOX 309Mo AWS SFA 5.4 : E 309MoL-16 WELDING ELECTRODE

 OERLIKON INOX 309Mo
For welding stainless and heat resisting steels, rutile covering

Application & Properties:
Electrode for joining dissimilar steels (austenitic steels to ferritic steels) and for austenitic claddings. Weld metal consists of austenite with approx. 15% delta-ferrite.  Claddings on unalloyed and low-alloy steels are already corrosion resistant in the first layer. Highest operating temperature for joints between dissimilar steels is +300oC. In case of higher temperatures, use OERLIKON SUPRANEL 600 electrodes. Fine metal droplet transfer, good fusion of joint faces, finely rippled bead surface, easy slag removal, easy arc striking and restriking.

Aplikasi & Penggunaan:
Kawat las untuk penyambungan baja yang tidak sama jenisnya (baja austenite dengan baja ferrite). Alur las memiliki struktur austenite dengan kandungan delta ferrite +/- 15%. Temperatur operasi untuk penyambungan baja yang berbeda jenisnya bisa mencapai hingga temperatur 300oC. Penetrasinya dalam, karakter penyambungannya sangat baik, alur lasnya halus dan bersih, pelepasan teraknya sangat mudah, kestabilan nyala api dan restrikingnya mudah.

International Standards:
AWS SFA 5.4 : E 309MoL-16
DIN EN 1600 : E 23 12 2 L R 12
DIN 8556 : E 23 13 2 L R 23

Mechanical Properties:

Yield strength : 420 N/mm2
Tensile strength : 640 N/mm2
Elongation : 30 %
Impact Charpy (+20oC) : 50 J

Chemical Analysis (%):
C: 0,025 Mn: 0,7 Si: 0,9
Cr: 22,5 Ni: 13,5 Mo: 2,6

 Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON CITOCHROMAX N AWS SFA 5.4 : E 307-15 WELDING ELECTRODE

 OERLIKON CITOCHROMAX N
For welding stainless and heat resisting steels, basic covering

Application & Properties:
Electrode for joining dissimilar steels and depositing claddings on ferritic steels. The weld metal consists of austenitic Cr-Ni-Mo steel with possible small amounts of delta-ferrite. It is non-scaling up to +850oC. The weld metal is highly crack-resistant and therefore suited to joining difficult-to-weld steels and depositing stress-relaxing buffer layers on crack sensitive base metal or underneath hard facing deposits. Highest operating temperature for dissimilar steel joints is +300oC. In case of higher temperatures, use OERLIKON SUPRANEL 600 electrodes. Weld metal work-hardens.
 
Aplikasi & Penggunaan:
Kawat las untuk penyambungan baja yang tidak sama jenisnya. Hasil las memiliki struktur austenite chromium-nikel-molybdenum dan sedikit mengandung struktur delta ferrite. Ketahanannya terhadap scaling bisa mencapai hingga temperatur 850oC. Kawat las memiliki ketahanan terhadap keretakan yang sangat baik dan sangat cocok untuk penyambungan baja yang sulit dilas serta sebagai buffer layer yang ulet untuk pengelasan baja yang sangat sensitif terhadap keretakan, atau sebagai landasan sebelum dilakukan pengelasan hard facing. Temperatur operasi untuk penyambungan baja yang tidak sama jenisnya bisa mencapai hingga temperatur 300oC. Hasil las dapat di-work-hardening.

International Standards:
AWS SFA 5.4 : E 307-15
DIN EN 1600 : E 18 8 Mn B 22
DIN 8556 : E 18 8 Mn B 20 +

 Mechanical Properties:
Yield strength : 400 N/mm2
Tensile strength : 650 N/mm2
Elongation : 35 %
Impact Charpy
+20oC : 100 J
-60oC : 60 J

Chemical Analysis (%):
C: 0,12 Mn: 6 Si: 0,4
Cr: 19 Ni: 9

 Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON CITORAIL DIN 8555 : E 1 - UM - 300 WELDING ELECTRODE

OERLIKON CITORAIL
For wear resisting hardsurfacing applications, basic covering

Application & Properties:
Thick basic-covered electrode for producing hard facing deposits of medium hardness, which can be machined by chip-forming. Particularly suited for wear resisting parts subjected to heavy impact and shock. OERLLION CITORAIL can be easily welded in all positions, except vertical-down. Weld metal is crack resistant and free of pores. Suitable for: Reconditioning of rails, rail crossings, switch points, sprockets and wearing parts, such as: rope pulleys, tumblers, rollers, caterpillar track rollers and links, wheel flanges, stud links and others.

Aplikasi & Penggunaan:
Kawat las dengan coating type basic yang tebal untuk pengelasan hard facing dengan kekerasan sedang yang dapat dibubut atau dibentuk. Sangat cocok untuk komponen yang memerlukan ketahanan terhadap gesekan serta benturan yang berat. Kawat las OERLIKON CITORAIL dapat digunakan pada segala posisi, kecuali vertical-down. Alur las bebas dari keretakan dan pori. Sangat cocok untuk perbaikan: rel kereta api, crossing pada rel kereta api, switch points, sprocket, dan komponen-komponen yang aus karena gesekan seperti:  pulleys, tumbler, roller, caterpillar track rollers and links, wheel flanges, stud links, dll.

International Standards:

DIN 8555 : E 1 - UM - 300

Mechanical Properties:

Hardness: 275 - 325 HB

Chemical Analysis (%):

C: 0,1 Mn: 0,9 Si: 0,6
Cr: 3,2

Redrying: 200oC for 2 hrs

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com

OERLIKON CITODUR SM DIN 8555 : E 6 - UM - 600 WELDING ELECTRODE

 OERLIKON CITODUR SM
For wear resisting hardsurfacing applications, rutile covering

Application & Properties:
Thick rutile coated SMAW electrode for hardsurfacing rollers in sugar mills. Restrikes automatically even on wet base materials,  allows  to  deposit efficient shaped dots,  good weld bead aspect even at high travel speed, 200% recovery. Suitable for: mill rollers and roller flange in sugar manufactories.

Aplikasi & Penggunaan:
Kawat las dengan coating type rutile yang tebal untuk melapisi roller-roller pada pabrik gula. Restrikingnya sangat mudah bahkan pada material yang basah, deposit lasnya berfungsi khusus untuk pengasaran roller roller pada pabrik gula, alur lasnya sangat baik walaupun kecepatan pengelasannya tinggi, efisiensi pengelasannya: 200%. Sangat cocok untuk pengelasan roller-roller dan komponen-komponen lainnya pada pabrik gula.

International Standards:
DIN 8555 : E 6 - UM - 600

Mechanical Properties:
Hardness : 53 HRC (1 layer)
62 HRC (2 layers)

Chemical Analysis (%):
C: 4,4 Mn: 2,3 Ni: 2,9
Cr: 27,8

Redrying: 200oC for 2 hrs

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com

OERLIKON CITOMANGAN DIN 8555 : E 7 - UM - 200 KP WELDING ELECTRODE

 OERLIKON CITOMANGAN
For wear resisting hardsurfacing applications, basic covering

Application & Properties:
Basic covered austenitic manganese steel electrode for wear resisting hard facing deposits. Weld metal will adopt high hardness by cold working. It is therefore particularly suited for parts which are subjected mainly to wear caused by heavy impact and shock. During welding, the workpieces should not become too hot and, if necessary, be allowed to cool down. When welding large workpieces made of austenitic manganese steel, such as crusher jaw plates, it is advisable to weld them in a water bath. High welding currents and wide-weave beads must be avoided. When building up various layers, it is good practice depositing a buffer layer with  OERLIKON CITOCHROMAX N weld metal. When making joint welds on austenitic manganese steel, it is preferable to use OERLIKON CITOCHROMAX N electrode. Suitable for: Hardfacing and repair welding of wear resisting parts made of austenitic manganese steel, such as crusher jaw plates, crusher cones, pulverizing hammers, beating arms and others.

Aplikasi & Penggunaan:
Kawat las austenite manganese dengan coating type basic untuk pengelasan hard facing. Hasil las memiliki kekerasan yang tinggi. Sangat cocok untuk komponen-komponen yang aus karena mengalami benturan yang berat. Untuk pengelasan banyak layer, disarankan untuk memakai buffer layer OERLIKON CITOCHROMAX-N. Untuk penyambungan baja manganese austenite, disarankan untuk menggunakan kawat las OERLIKON CITOCHROMAX-N. Sangat cocok untuk perbaikan komponen baja manganese austenite yang memerlukan ketahanan terhadap gesekan, seperti: crusher jaw plates, crusher cones, pulverizing hammers, beating arms, dll.

nternational Standards:
DIN 8555 : E 7 - UM - 200 KP

Mechanical Properties:
Hardness : 200 HB (as welded)
400 - 500 HB
(after work hardening)

Chemical Analysis (%):
C: 0,6 Mn: 14 Ni: 4
Cr: 4

Redrying: 200oC for 2 hrs

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com

OERLIKON CITODUR 600B DIN 8555 : E 6 - UM - 60 WELDING ELECTRODE

OERLIKON CITODUR 600B
For wear resisting hardsurfacing applications, basic covering
 
Application & Properties:
Thick basic-covered electrode for depositing tough and wear resisting overlays on structural members subjected to severe wear. The weld metal is free of cracks and pores and resistant to impact and shock. It can be machined only by grinding. Only in case of very crack sensitive base metals, a tough buffer layer, made with OERLIKON CITOCHROMAX N electrodes, is required. Multi-layer deposits will be free of cracks, even without depositing intermediate buffer layers. Suitable for: Hard facing excavator parts, bucket edges and bucket teeth, drilling bits, coal planes, conveyor screws, polygon edges, crusher jaws and cones.

Aplikasi & Penggunaan:
Kawat las dengan coating type basic yang tebal yang menghasilkan alur las yang ulet untuk komponen yang memerlukan ketahanan terhadap benturan. Alur las bebas dari keretakan dan pori, serta memiliki ketahanan terhadap pukulan dan benturan. Hasil las dapat dibentuk dengan cara digerinda. Untuk material yang sensitif terhadap keretakan dibutuhkan buffer layer yang ulet: OERLIKON CITOCHROMAX N. Lapisan dengan banyak layer bebas dari keretakan, walaupun tanpa menggunakan buffer layer. Sangat cocok untuk perbaikan: excavator parts, bucket edges and bucket teeth, drilling bits, coal planes, conveyor screws, polygon edges, crusher jaws and cones.

International Standards:
DIN 8555 : E 6 - UM - 60

Mechanical Properties:
Hardness : 57 - 62 HRC (as welded)

Chemical Analysis (%):
C: 0,5 Mn: 0,3 Ni: 0,4
Cr: 7 Mo: 0,5 V: 0,5

Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON CITODUR V 1000 DIN 8555 : E 10 - UM - 60 R WELDING ELECTRODE

 OERLIKON CITODUR V 1000
For wear resisting hardsurfacing applications, rutile covering

Application & Properties:
Thick rutile-covered high alloy electrode depositing hypereutectic chromium hard metal. It is suitable for producing highly wear resisting deposits subject to abrasion by mineral particles. The typical transverse cracks appearing in this hard facing weld metal are not detrimental to abrasion resistance. However, the weld metal is not resistant to impact and shock, and is machinable only by grinding. On difficult-to-weld steels, a buffer layer made with OERLIKON CITOCHROMAX N electrodes is required. OERLIKON CITODUR V-1000 produces very smooth weld beads with flat penetration. Metal recovery is approx. 160%.

Aplikasi & Penggunaan:
Kawat las dengan coating type rutile yang menghasilkan alur las chromium hyper-eutectic yang sangat keras. Sangat cocok untuk melapisi komponen yang memerlukan ketahanan terhadap gesekan oleh abrasi mineral. Hasil las tidak memiliki ketahanan terhadap pukulan dan benturan, dan hanya dapat dibentuk dengan cara digerinda. Untuk material yang sulit dilas, dibutuhkan buffer layer yang ulet: OERLIKON CITOCHROMAX N. Kawat las OERLIKON CITODUR V-1000 menghasilkan alur las yang halus dengan penetrasi yang datar. Efisiensi pengelasan: 160%.

International Standards:
DIN 8555 : E 10 - UM - 60 R

Mechanical Properties:
Hardness : 58 - 62 HRC (as welded)

Chemical Analysis (%):
C: 4,3 Cr: 35

Redrying: 200oC for 2 hrs

Contact Person:  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206

Email                 : setyo.marketing@yahoo.com

OERLIKON BRONZE AWS SFA 5.6 : E Cu Sn C WELDING ELECTRODE

 OERLIKON BRONZE
For welding copper and its alloys

Application & Properties:
Basic tin-bronze for assembly and surfacing weld on copper alloys and suitable for depositing a bronze layer on a steel, cast steel, and cast steel. Particularly recommended for surfacing welds on bronze bearings in machine building. Suitable for assembly and surfacing weld on tin-bronze materials, red brass, and copper as well as for depositing a bronze layer on a steel, cast steel, and cast iron.

Aplikasi & Penggunaan:
Kawat las timah-tembaga dengan coating type basic untuk perbaikan dan melapisi material yang terbuat dari paduan tembaga dan juga cocok untuk membuat lapisan tembaga pada baja karbon, baja ancuran. Kawat las ini direkomendasikan untuk pengelasan komponen-komponen mesin atau bearing yang terbuat dari tembaga. Sangat cocok untuk pengelasan material-material yang terbuat dari timah-tembaga, kuningan, dan tembaga murni.

International Standards:
AWS SFA 5.6  : E Cu Sn C
DIN 1733        : E Cu Sn 8

Mechanical Properties:
Tensile strength : 300 - 350 N/mm2
Hardness           : 70 - 110 HV

Chemical Analysis (%):
Cu: 91 Sn: 7,5 Mn: 0,4 P: 0,3

Redrying: 200oC for 2 hrs

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com
.

OERLIKON CITOFONTE Ni AWS SFA 5.15 : E NiC1 WELDING ELECTRODE

OERLIKON CITOFONTE Ni
For heterogeneous welding of cast iron, basic covering

Application & Properties:
Electrode having a pure nickel core wire for welding cast iron without or with low preheating (max. +300o C). For repair welding of cracked cast iron parts or joining components made of steel, copper of nickel materials to castings. Easy arc striking and restriking, stable arc, smooth bead surface. Weld short beads, about 30 to 50 mm long. In order to reduce weld residual stresses, hammer-peen welds slightly before cooling. Weld metal is machinable. Electrode suited to welding cast iron with lamellar graphite, white and black heart malleable and nodular cast iron.
 
Aplikasi & Penggunaan:
Kawat las dengan kawat inti nikel murni untuk pengelasan ancuran dengan atau tanpa preheating / pemanasan awal 300oC. Sangat cocok untuk pengelasan ancuran atau penyambungan material yang terbuat dari baja dan tembaga ke ancuran. Kestabilan nyala apinya sangat baik, alur lasnya halus. hasil las dapat dibubut. Kawat las sangat cocok untuk pengelasan baja ancuran lamelar graphite, baja ancuran putih, baja ancuran hitam-malleable, baja ancuran nodular.

International Standards:
AWS SFA 5.15 : E NiC1
DIN 8573 : E Ni BG 22

Mechanical Properties:
Hardness : 140 HB
Yield strength : 200 N/mm2
Tensile strength : 400 N/mm2
Elongation : 5%

Chemical Analysis (%):
C: 0,5 Ni: Basis Fe: 2

Redrying: 100 - 110oC for 1 hr

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com

.

OERLIKON CITOFONTE Mo AWS SFA 5.15 : E NiCu-B WELDING ELECTRODE

OERLIKON CITOFONTE Mo
For heterogeneous welding of cast iron, basic covering


Application & Properties:
Electrode having a nickel-copper core wire for welding cast iron without or with low preheating (up to +300oC). Iron admixture from base metal should be kept low. Thus, electrode is preferably used for making filler and cover passes or for filling-up shrinkage cavities. It is advisable to "butter" groove faces with OERLIKON CITOFONTE Ni. Weld metal closely matches colour of base metal. Easy arc striking and restriking, stable arc, smooth bead surface. Weld metal is machinable. Weld short beads. Well-suited to welding cast iron with lamellar graphite, white and black heart malleable cast iron, nodular cast iron.

Aplikasi & Penggunaan:
Kawat las dengan kawat inti nikel-tembaga untuk pengelasan ancuran dengan / tanpa pemanasan awal (sampai 300oC). Sangat cocok untuk pengelasan filler & cover pass. Alur las warnanya mendekati dengan warna dari base metal  Striking & restrikingnya mudah, kestabilan nyala apinya baik, alur lasnya halus. Hasil las dapat dibubut. Kawat las sangat cocok untuk pengelasan baja ancuran lamelar graphite, baja ancuran putih, baja ancuran hitam-malleable, baja ancuran nodular.

International Standards:
AWS SFA 5.15 : E NiCu-B
DIN 8573 : E NiCu BG - 22

Mechanical Properties:
Hardness : 150 HB
Yield strength : 220 N/mm2
Tensile strength : 400 N/mm2
Elongation : 15%

Chemical Analysis (%):C: 0,5 Ni: Rest Fe: 4
Cu: 30

Redrying: 100 - 110oC for 1 hr

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com
.

OERLIKON SUPERFONTE NiFe AWS SFA 5.15 : E NiFeC1 WELDING ELECTRODE

 OERLIKON SUPERFONTE NiFe
For heterogeneous welding of cast iron, basic covering

Application & Properties:
Electrode having a nickel-iron core wire for welding cast iron without or with low preheating of up to +300oC. The weld metal features a low coefficient of thermal expansion and as a result, little shrinkage. It has higher strength properties than pure nickel weld metal and is therefore preferable used for welding nodular cast iron, white and black heart malleable cast iron, as well as austenitic nodular cast iron or joining these metals to components made of steel, copper or nickel materials. Easy arc striking and restriking, stable arc, smooth bead. Weld metal is machinable. Weld short beads.

Aplikasi & Penggunaan:
Kawat las dengan kawat inti ferro-nikel untuk pengelasan ancuran dengan atau tanpa pemanasan awal hingga 300oC. Alur las memiliki keunggulan: koefisien muai panasnya yang rendah, sehingga shrinkagenya sangat kecil. Kekuatannya lebih tinggi dari kawat las nickel murni sehingga sangat cocok untuk pengelasan baja ancuran type nodular, putih, dan hitam malleable, serta ancuran nodular austenite atau penyambungan material ferro-nikel dengan besi, tembaga atau dengan material nikel. Striking dan restrikingnya sangat mudah, kestabilan nyala apinya sangat mudah, alur lasnya sangat baik. Hasil las dapat dibubut.

International Standards:
AWS SFA 5.15  : E NiFeC1
DIN 8573          : E NiFe-1 BG 22

Mechanical Properties:
Hardness           : 170 HB
Yield strength    : 300 N/mm2
Tensile strength : 450 N/mm2
Elongation         : 10%

Chemical Analysis (%):
C: 0,5 Ni: 53 Fe: Rest
Redrying: 100 - 110oC for 1 hr

 

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com
.

OERLIKON CITOCUT GOUGING WELDING ELECTRODE

OERLIKON  CITOCUT 
For cutting, chamfering, gouging, beveling, and channeling ferrous and non-ferrous metals

Application & Properties:
For chamfering, gouging, beveling, and channeling ferrous and non-ferrous metals using the arc. No oxygen or air required. Special coating makes electrode highly heat resistant and concentrates arc-force right on point of application. Chamfered surface requires little or no finishing operation. Some specific uses are high speed removal of excess metal, gouging out old or bad welds, preparing joints to be welded in position, rooting out high chrome deposits on deeper teeth, armor plates, etc. prior to hardsurfacing, removal of most of unwanted metal before final machining operations.

Aplikasi & Penggunaan:
Kawat las ini berfungsi untuk memotong, membuang alur las dari material yang terbuat dari besi maupun yang bukan dari besi. Dalam penggunaannya tidak diperlukan oksigen maupun udara. Kegunaan khusus dari kawat las ini yaitu: membuang alur las yang berlebihan, membuang alur las yang salah, mempersiapkan sambungan yang akan dilas, membuang alur las hardfacing yang keras karena mengandung unsur chromium, seperti: bucket teeth, armor plates, dll, dan untuk membuang alur las yang tidak diinginkan sebelum dilakukan finishing.

Redrying: Do not redry!

Contact Person :  Setyo Nugroho, ST

No.HP               :  0815 84104675

Telp                   : 021-33038206 

Email                 : setyo.marketing@yahoo.com
.